Product Details
Technical Parameters:
Items
|
Part A
|
Part B
|
Before curing
|
Appearance
|
white
|
brown
|
Viscosity(mPa.s)
|
22000±5000
|
200±50
|
Density(g/cm3)
|
1.70±0.05
|
1.22-1.25
|
Use ration by weight A:B
|
6:1
|
Specification
|
Viscosity after mixing
(mPa.s)
|
3500±500 adjustable
|
Operation time(min,25℃)
|
30 adjustable
|
Turnover time(min,25℃)
|
150 adjustable
|
Curing time(h,25℃)
|
24
|
After curing
|
Light yellow
|
Shear strength(N/mm)
|
19.85
|
Max peel force(N)
|
990.63
|
Max peel strength(N/mm)
|
99.06
|
Average peel force(N)
|
717.77
|
Average peel strength(N/mm)
|
71.78
|
Min peel force(N)
|
455.87
|
Min peel strength(N/mm)
|
45.59
|
Â
Â
Class
|
Grade
|
Efficiency
|
Resistance
|
Tensile Strength
|
Thickness
|
Basic Weight
|
Stiffness
|
HEPA
0.3mm
@5.3cm/s
|
H14
|
≥99.995%
|
≤420Pa
|
1.0-1.25KN/m
|
0.33±0.02mm
|
74±4g/m2
|
mg≥1000
|
H13
|
≥99.97%
|
≤330Pa
|
0.9-1.20KN/m
|
0.33±0.02mm
|
74±4g/m2
|
mg≥1000
|
H12
|
≥99.8%
|
≤260Pa
|
0.9-1.20KN/m
|
0.33±0.02mm
|
74±4g/m2
|
mg≥1000
|
H11
|
≥98%
|
≤180Pa
|
0.9-1.20KN/m
|
0.33±0.02mm
|
74±4g/m2
|
mg≥1000
|
H10
|
≥94%
|
≤120Pa
|
0.9-1.20KN/m
|
0.33±0.02mm
|
74±4g/m2
|
mg≥1000
|
ASHRAE
0.4mm
@5.3cm/s
|
F9
|
≥95%
|
≤80Pa
|
0.9-1.15KN/m
|
0.33±0.02mm
|
70±4g/m2
|
mg≥900
|
F8
|
≥90%
|
≤60Pa
|
0.9-1.15KN/m
|
0.33±0.02mm
|
70±4g/m2
|
mg≥900
|
F7
|
≥80%
|
≤40Pa
|
0.9-1.15KN/m
|
0.33±0.02mm
|
70±4g/m2
|
mg≥900
|
F6
|
≥60%
|
≤25Pa
|
0.9-1.15KN/m
|
0.33±0.02mm
|
70±4g/m2
|
mg≥900
|
Â
Specifications:
Model
|
3016A
|
Main Components
|
polyolefin
|
Color
|
white
|
- The product is a polymerized heat with 100% solid content molten adhesive, used as a solid state at room temperature
- 100% solid content, green and environmental protection Good adhesive properties for the filter element origami Lower adhesive temperature Better processing performance.
- No partition plate suitable for purification or other works Air filter molding, bonding and reinforcement.
Â
Softening Point (GB/T-15332) 110±5℃ viscosity /180℃ (GB/T-2794) 3500±800cps curing time
Â
Instructions for using:
Hotmelt tank: 140-160℃;hose:130-150℃; gun:120-135℃
Â
Storage:
- Store them in a dry, cool place and avoid them Direct sunlight, with a storage period of two years
- Do not mix them with other adhesives
- Wear personal protective equipment when operating
- to prevent high equipment Warm scald Advanced first use
- to avoid long-term glue in high temperature Stay and aging failure Please sure the bonding substrate surface is not contaminated
- To achieve a good bonding effect Long time shutdown should be timely emptied and washed machine.
- The product color will depend on the raw material batch Slightly different, but will not affect the usability ability